Growth of Defect-Free GaAsSbN Axial Nanowires via Self-Catalyzed Molecular Beam Epitaxy

Bandgap reduction of 10% by incorporation of a dilute amount of N is reported for the first time, in axial GaAsSb nanowires (NWs) grown on Si (111) via Ga-assisted molecular beam epitaxy. Impact of N incorporation on the surface morphology, NW growth kinetics, and their structural and optical properties were examined. Dilute nitride NWs with Sb composition of 7 at. % did not exhibit any noticeable planar defects, as revealed by the absence of satellite twin peaks in the selected-area diffraction pattern and high-resolution transmission electron microscopy imaging. Point defects were also minimal in as-grown dilute nitride NWs, as ascertained from the comparison of low-temperature photoluminescence spectra as well as the shape and shift of Raman modes, with in-situ annealed NWs in different ambients. Evidence of enhanced incorporation of N was found in the NWs in-situ annealed in N ambient, but with deteriorated optical quality due to simultaneous creation of N-induced defects. The lack of any noticeable defects in the as-grown GaAsSbN NWs demonstrates the advantage of the vapor-liquid-solid mechanism responsible for growth of axial configuration over the vapor-solid growth mechanism for core-shell NWs as well as their thin film counterpart, which commonly exhibit N-induced point defects.